The CY-LD03 nano particle composite electroplating coating has a more compact structure, which has better performance, higher hardness, better wear resistance, higher coating bonding strength, and an operating temperature of 400 degrees.

1、 Performance characteristics and functions

The Jiupeng brand CY-LD03 high corrosion resistant nickel plating nanocomposite electroplating slurry can make the nickel coating dense, crystallize finely, and reduce porosity by 50% through the action of nanomaterials.

The corrosion resistance of Jiupeng brand CY-LD03 nano electroplating slurry is 2-3 levels higher than that of the same thickness nickel layer. Hardness increased by 50% and wear resistance increased by 10 times. The deep plating ability and leveling ability have been significantly improved, the process range has been widened, the comprehensive cost of nickel plating has been reduced, and production efficiency has been improved.

Jiupeng brand CY-LD03 nano electroplating slurry can save 30% nickel.

2、 Comparison of Coating Properties

Using the blue dot experiment method and soaking in a 5% sodium chloride solution.

Number: Nickel plating solution, coating thickness:

(μ m) porosity

Corrosion resistance time per cm2 (hours)

Large area of the first rust spot appears

corrosion

1 watt solution with rough appearance 5.41.5832

2 watts solution with additives has a smooth appearance

Bright 5.61.6935

3 watt solution with CY-D03 for smooth and bright appearance 6.00.82698

3、 Usage

1. Full bright nickel: cylinder opening volume of 3-5ml/L, consumption volume of 200ml/KAH

Under the condition of maintaining the original corrosion resistance requirements, the electroplating time can be reduced by 20-30%, and the automatic line can reduce the current by 20-30%.

2. Semi bright nickel: cylinder opening capacity of 4-6ml/L, consumption of 300ml/KAH, fine crystallization of the coating, good brightness and leveling, and improved corrosion resistance.

3. Rolling nickel plating: With a cylinder opening volume of 5-6ml/L and a consumption of 400ml/KAH, the rolling plating time is shortened by 20-30%, improving production efficiency and reducing overall costs. However, the corrosion resistance of the product remains unchanged, and the deep plating ability and brightness are significantly improved.

4、 Packaging in 25 kg drums