3Y yttrium stabilized nano zirconia cy-R200y3

3Y yttrium stabilized nano zirconia cy-R200y3

share

3Y yttrium stabilized nano zirconia cy-R200y3

  • Detail
  • Parameters

3

Yttrium stabilized nano zirconia




Hangzhou Jiupeng New Materials



essential information:


3Y yttrium stabilized nano zirconia has a 99.9% market share in the European and American markets of medical bioceramics, mainly used in dental crowns, bridges, full crowns, dental roots, abutments, and human joints


3Y yttrium stabilized nano zirconia is currently the most widely used biomedical material. The characteristics of yttrium stabilized zirconia used in high transparency dentures not only lie in its high fracture strength (>1000 MPa) and high fracture toughness (>10 MPa · m1/2), significantly slowing down the behavior of slow cracking, but also in the ceramic blocks fired from yttrium stabilized zirconia used in high transparency dentures, which have high transparency, strong jade texture, and high whitening, and can match well with the color of human teeth. And it is extremely suitable for milling using manual grinders or CAD/CAM equipment.


Compared with traditional dental ceramic materials, yttrium stabilized zirconia polycrystalline ceramics (Y-TZP) for high permeability dentures using yttrium oxide (Y2O3) as a stabilizer have received widespread attention due to the stress induced phase transition toughening effect of metastable tetragonal zirconia to monoclinic zirconia (m-ZrO2), which leads to higher toughness. High transparency yttrium stabilized zirconia for dentures is an excellent high-tech biomaterial, and it is currently recognized that both the price and quality of denture production are better than those of high transparency yttrium stabilized zirconia for dentures.


Technical indicators:


型号

cy-R200K

cy-R200KR


气流粉

造粒粉

晶相

3Y四方相

3Y四方相

ZrO2% (+ HfO2)

94.7

94.7

Y2O3(wt%)

5.3±0.3

5.3±0.3

Al2O3% ≤

0.05

0.05

SiO2%≤

0.005

0.005

Fe2O3%≤

0.001

0.001

CaO%≤

0.005

0.005

MgO%≤

0.005

0.005

TiO2%≤

0.002

0.002

Na2O%≤

0.005

0.005

Cl- %≤

0.1

0.1

灼减%≤

0.8

0.8

平均粒径

50-80nm

50-80um

瓷块的半透明度

3.2x10^3 lux

3.2x10^3 lux

瓷块经冷等静压后密度

6.08g/cm3

6.08g/cm3

挠曲强度

>1000MPa

>1000MPa


包装:25公斤每袋/桶


型号
cy-R200y3